Synthesis of vanadium oxide nanofibers and tubes using polylactide fibers as template

A new method to produce vanadium oxide nanofibers with dimensions <140 nm and tubes is reported. Vanadium oxide was coated on polylactide fibers by a sol–gel method using a reaction mix of ammonium vanadate and acetic acid as starting materials and water as solvent. Vanadium oxide tubes, of about 1 μm in diameter, were formed when this coated fiber was heated in nitrogen and oxygen at 300 and 250 °C for 1 h. Hydrothermal treatment of the polylactide fibers with the reaction mix at 160 °C for 12 h followed by heating in oxygen at 300 °C for 1 h formed vanadium oxide nanofibers, 60–140 nm in width and several microns in length. Electrochemical studies reveal that these vanadium oxide nanofibers are redox active and readily undergo reversible reactions with lithium in non-aqueous cells.