Amelioration of the hydriding and dehydriding kinetics of Mg by pulverization and the formation of Mg2Ni hydride
Author/Authors :
Song، نويسنده , , MyoungYoup and Kwon، نويسنده , , SungNam and Mumm، نويسنده , , Daniel R.، نويسنده ,
Issue Information :
روزنامه با شماره پیاپی سال 2007
Pages :
9
From page :
912
To page :
920
Abstract :
The addition of an oxide Fe2O3 is considered to increase the hydriding rate of Mg by pulverization, and the addition of Ni to increase the hydriding and dehydriding rates by the formation of Mg2Ni hydride. The sample Mg–10 wt.% (Fe2O3, Ni) was prepared by grinding Mg mechanically under H2 (reactive mechanical grinding) with nano-structured Fe2O3 particles and Ni. The as-milled sample absorbed 4.24 wt.% hydrogen at 593 K under 12 bar H2 for 60 min. Its activation was accomplished after two hydriding–dehydriding cycles. The activated sample absorbed 4.05 wt.% hydrogen at 593 K, 12 bar H2 for 60 min and desorbed 3.05 wt.% hydrogen at 593 K, 1.0 bar H2 for 60 min. After hydriding–dehydriding cycling, Mg2Ni is formed by the reaction of Mg with Ni, Fe2O3 is reduced, and a small fraction of Mg is oxidized.
Keywords :
A. Hydrides , C. X-ray diffraction , D. Catalytic properties , D. Phase transitions