Conductivity of reduced La2Mo2O9 based oxides: The effect of tungsten substitution

The electrical properties of reduced LAMOX-type oxides (La1.9Y0.1Mo2−yWyO9−δ with y = 0, y = 0.5, y = 1.0) were investigated by complex impedance spectroscopy. educed at 605 °C in hydrogen, La1.9Y0.1Mo2O9−δ is 10 times and 3 × 105 times more conductive at 605 and 180 °C, respectively, than in air at the same temperatures. The conductivity curve presents a low slope (0.37 eV versus 1.2 eV in air). s, the stabilising effect of tungsten against reduction is evidenced, in good agreement with previous reports. oxygen partial pressures however (PO2 < 10−18 Pa), the decomposition of the materials is detected, whatever the tungsten content (0 ≤ y ≤ 1 in La1.9Y0.1Mo2−yWyO9−δ). This observation points out the efficiency limit of Mo6+/W6+ substitution to stabilise the structure against reduction, and the limit for an application as IT-SOFC electrolyte. r, given the high electronic conductivity upon reduction, the application of these materials in IT-SOFC electrodes could be considered.