Microstructure and mechanical properties of Pt-added and Pd-added Zr-20Nb alloys and their metal release in 1 mass% lactic acid solution

The effects of Pt and Pd addition to a Zr-20Nb alloy on its microstructure and mechanical property, as well as the elution of metals from the alloys in lactic acid solution, were investigated. The microstructure was characterized with an X-ray diffractometer (XRD), an optical microscope (OM), and a transmission electron microscope (TEM). The mechanical properties were evaluated by a tensile test. The β phase is dominantly observed in the Zr-20Nb as well as in the Pt-added and Pd-added Zr-20Nb alloys. Needle-like microstructures are observed in equiaxed grains in all alloys. Pd addition to the Zr-20Nb alloy suppresses ω phase formation more than Pt addition does. The 0.2% offset yield strength and the ultimate tensile strength of the Pt-added and Pd-added Zr-20Nb alloys increase with the Pt and Pd concentrations. XRD analysis revealed that the lattice parameter of β-Zr in the Pt-added and Pd-added Zr-20Nb alloys decreases with the Pt and Pd concentrations. Pt and Pd solute in β-Zr as a substitutional element and contribute to the increase in the strength by solid solution hardening. The addition of 2Pt and 2Pd to the Zr-20Nb alloy also improves metal elution from the alloys in lactic acid solution.