New hydrogels based on maleilated collagen with potential applications in tissue engineering

New hydrogels based on maleic anhydride (MA) modified collagen were prepared with the aim of overcoming the high degradation rate displayed by collagen that is not otherwise chemically crosslinked. Semi-interpenetrated matrices were obtained by free radical polymerization of maleilated collagen (CM) and 2-hydroxyethyl methacrylate (HEMA) in the presence of ammonium persulfate (APS) and N,N,N′,N′-tetramethylethylenediamine (TEMED) as initiating system. The resulting matrices (CMH) had a sharp decrease in degradation, when compared to pure collagen. FTIR and H1 NMR spectroscopies were used to confirm the incorporation of MA on the collagen peptide chains. The final composition of CMH was found to be strongly dependent by the concentration of maleilated collagen. The morphology of the hydrogels was studied by Scanning electron microscopy (SEM) and the macro-gel structure was confirmed. Water uptake of the synthetised hydrogels is influenced by both composition and the porosity of the matrices.