In vitro degradation behavior and biocompatibility of Mg–Nd–Zn–Zr alloy by hydrofluoric acid treatment

In this paper, Mg–Nd–Zn–Zr alloy (denoted as JDBM) coated with hydrofluoric acid (HF) chemical conversion film (MgF2) was researched as a potential biodegradable cardiovascular stent material. The microstructures, in vitro degradation and biocompatibility were investigated. The field emission scanning electron microscopy (FE-SEM) and X-ray photoelectron spectroscopy (XPS) showed that a compact MgF2 film was formed on the surface of JDBM. The corrosion rate decreased in artificial plasma from 0.337 to 0.253 mm·y− 1 and the electrochemical measurement demonstrated that the corrosion resistance of JDBM alloy could be obviously improved due to the protective MgF2 film on the surface of the substrate. Meanwhile, the hemolysis ratio of JDBM decreased from 52.0% to 10.1% and the cytotoxicity met the requirement of cellular application after HF treatment. In addition, JDBM and MgF2 film showed good anti-platelet adhesion, which is a very favorable property for implant material in contact with blood directly.