Oxidation behaviour of ledeburitic steels for hot rolls

The oxidation behaviour of two high speed steels (HSS) employed for the production of hot rolls was studied. The steels have slightly different chromium contents and volume fractions of primary carbides. Because oxidation nucleates at the matrix–carbide interfaces and propagates in the matrix without involving the carbides, the oxide scale grows less uniform. All the primary carbides have a higher Cr content than the matrix; therefore they tend to reduce the oxidation resistance. The slight differences in chromium content and in carbide volume fraction are responsible for the different oxidation resistance at 600 and 700°C, whilst at 500°C the two steels have almost the same resistance.