Laser boronising of Ti–6Al–4V as a result of laser alloying with pre-placed BN

This paper discusses the effect of CO2 laser alloying of pre-placed BN coating with Ti–6Al–4V alloy. The formation of titanium boride and titanium nitride investigated using energy dispersive X-ray diffraction (EDXRD) result were related to the microhardness and microstructure. The nitrogen and boron diffusion during the laser boronising process identified using secondary ion mass spectrometry (SIMS) and X-ray photoelectron spectrometry (XPS) analysis was compared with the EDXRD results. The surface hardness HV1500–1700 observed at the boronised layer was five to six times higher than that of untreated Ti–6Al–4V alloy. This was compared with needle platelet and dendrite type microstructures. Theoretically estimated surface temperature values were used to interpret the compound formation in the laser alloyed layer.