The influence of thermo-mechanical processing on the microstructure of steel 20MoCrS4

The influence of thermo-mechanical processing (TMP) on the microstructure and mechanical properties of 0.22%C–0.87%Mn–0.73Cr–0.40Mo steel was investigated. The transformation CCT diagram and CCCT diagram were determined by dilatometric measurements. Hot deformation before austenite decomposition slightly accelerates ferritic transformation, retards bainitic reactions and decreases the bainite start temperature. Special methods of TMP were performed consisting of hot and/or warm compression deformations and dwell at an elevated temperature. The microstructure was studied using metallography and transmission electron microscopy. The compression deformation results in a remarkable refinement of the microstructure and an improvement of mechanical properties. Warm deformation followed by dwell at 470 °C was found to be suitable for an increase of tensile strength and notch toughness; the corresponding microstructure is a fine lath-like bainitic microstructure with a relatively homogeneous distribution of carbide particles.