High-temperature internal friction on TiAl intermetallics

In order to study the microscopic mechanisms controlling the plastic deformation at high temperature of two γ-TiAl alloys with nominal compositions: Ti–46.5Al–4(Cr, Nb, Ta, B) and Ti–45Al–(5–10)Nb (in at.%), internal friction (IF) measurements have been performed. A subresonant torsion pendulum has been used working in two different modes; changing the temperature between 300 and 1200 K at a constant frequency, and varying the frequency between 0.001 and 10 Hz at a fixed temperature. The resulting mechanical spectra show an anelastic relaxation peak at about 1060 K at 1 Hz in one of the alloys and a high-temperature background in both of them. Activation parameters of the loss peak have been calculated and an activation enthalpy of about 3.8 eV is obtained. The characteristics and a possible responsible mechanism for this relaxation peak are discussed.