Mechanical spectroscopy of thin layers of PPV polymer on Si substrates

The vibrating reed technique with electro“static” excitation and optical detection has been applied to investigate thin layers of poly-phenylene-vinylene, deposited by spin coating onto microfabricated Si cantilevers, during temperature cycling programs between 90 and 540 K at a rate of 1 K/min. From the vibration frequencies the Young’s modulus of the film can be estimated to be about 10 MPa at room temperature in the precursor phase (if prepared from a solution in toluene), which increases by conversion to the conjugate bonded polymer to about 50 MPa. The temperature dependence of internal friction reveals the processes of γ relaxations (crankshaft motion of side branches in the precursor) and β-relaxation (movements of a few monomer blocks in the polymer chain), as well as peaks indicating the structural transformations during conversion, and possibly a glass transition in the amorphous precursor phase. After conversion only the β-relaxation persists.