Mechanical spectroscopy in commercial Fe–6 wt.% Si alloys between 400 and 1000 K

Mechanical spectroscopy, neutron diffraction and differential scanning calorimetry (DSC) were performed on commercial Fe–6 wt.% Si alloy after quenching from high temperature. The damping spectrum shows a peak at around 800 K and an associated modulus defect. The modulus shows an increase during the second and subsequent heating runs. In addition, an anomaly in the modulus behavior has been found at around 400 K. Different thermal treatments allows to obtain two different recovery degrees of the quenched-in defects. The influence of the recovery degree on the 800 K internal friction peak and on the anelastic modulus has been evaluated and confirm the validity of the grain boundary mechanism associated to this peak. Experimental results are discussed on the basis of recovery and ordering processes.