Author/Authors :
Bilous، نويسنده , , O.O. and Artyukh، نويسنده , , L.V. and Bondar، نويسنده , , A.A. and Velikanova، نويسنده , , T.Ya. and Burka، نويسنده , , M.P. and Brodnikovskyi، نويسنده , , M.P. and Fomichov، نويسنده , , O.S. and Tsyganenko، نويسنده , , N.I. and Firstov، نويسنده , , S.O.، نويسنده ,
Abstract :
Boron alloying was found to have a beneficial effect on the plasticity of Ti–6Al and Ti–6Al–4V (wt.%) as-cast alloys for contents within the solubility limits (up to around 0.05 wt.%) and to enhance their strength and hardness HV in the range of the existence of metal-boride eutectic (up to 2.0 and 2.5 wt.% B studied, respectively). The boride reinforcement contributes much to the hardness and strength of the Ti–6Al and Ti–6Al–4V alloys, increasing them by 1.5–2 times at room temperature to 400 °C. Monovariant eutectics (Ti88.8Al11.2) + TiB and (Ti84.9Al11.4V3.7) + (Ti96.9V3.1)B were found to solidify at compositions Ti–6Al–1.8B and Ti–6Al–4V–2B (wt.%) and at temperatures of 1530 and 1515 °C, respectively.
Keywords :
Titanium alloy , Eutectic , Hardness , boride , Metal matrix composite , Phase equilibria