Investigations of MX and γ′/γ″ precipitates in the nickel-based superalloy 718 produced by electron beam melting

Samples with a composition similar to the nickel-based superalloy Inconel alloy 718 were produced by electron beam melting of prealloyed powder and investigated with respect to type and composition of the strengthening precipitates. The matrix consists of γ grains orientated in nearly the same direction, almost like a single crystal. Coarse precipitates (<2 μm), mostly of the (Ti,Nb)(C,N,B) type with B1 structure, are aligned along the growth direction. TEM and APFIM investigations of the γ matrix revealed very fine γ″ precipitates of around 5–10 nm in size. Additionally, at small angle grain boundaries, coarser γ″ precipitates of 50–100 nm in size have been observed. The 〈0 01〉 γ//〈0 0 1〉 γ″ and {1 0 0} γ//{1 0 0} γ″ orientation relationship between γ and γ″, known from literature [M. Sundararaman, P. Mukhopadhyay, Mater. Charact. 31 (1993) 191–196], was confirmed. Some γ′ precipitates of 2–5 nm in size were observed by means of FIM.