Development of new Al-based nanocomposites by mechanical alloying

Al-based binary (Al–Mg) and ternary (Al–Mg–Zr) elemental powder mixtures were mechanically alloyed to develop new Al–Mg–Zr nanocomposite materials. The phase evolution was studied in the as-milled and heat-treated powders by XRD and TEM/EDS analyses. For the binary Al–Mg alloy, the predominant phase was an Al(Mg) solid solution (SS) and an amorphous phase was not possible to be synthesized. Upon adding 5 at.% Zr to the Al–10Mg blended powder, some free Mg was present in addition to the formation of an Al(Zr,Mg)SS, which transformed to the Al3Zr intermetallic after annealing. When the Zr content was increased a nanocomposite of a solid solution and an intermetallic was obtained with considerable improvement in terms of structural stability and hardness. The presence of an oxide phase at 35% Zr might be responsible for the increased hardness in this particular alloy.