Effects of a laser surface processing induced heat-affected zone on the fatigue behavior of AISI 4340 steel

The effects of the heat-affected zone (HAZ) in AISI 4340 steel created by laser-surface alloying (LSA) on high-cycle fatigue behavior have been investigated. This research was performed by producing several lots of laser-processed AISI 4340 steel using different laser processing parameters, and then subjecting the samples to high-cycle fatigue and Knoop microindentation hardness studies. Samples of tested material from each lot were examined using scanning-electron microscopy (SEM) in order to establish the effects of laser processing on the microstructure of the fatigue-tested AISI 4340 steel. When these three techniques, microindentation hardness testing, high-cycle fatigue testing, and SEM, are combined, a mechanistic understanding of the effect of the HAZ on the fatigue behavior of this alloy might be gained. It was found that the HAZ did not appear to have an adverse effect on the high-cycle fatigue behavior of LSA-processed AISI 4340 steel.