Effect of coating on the creep behavior of the Ti–6Al–4V alloy

The influence of the plasma-sprayed coatings and of the atmosphere on creep of the Ti–6Al–4V alloy was investigated. Yttria partially stabilized zirconia (YSZ) with CoNiCrAlY bond coat was atmospherically plasma sprayed on Ti–6Al–4V substrates. Constant load creep tests were conducted on a standard creep machine in air and nitrogen atmospheres on uncoated samples and in air on coated samples, at stress levels of 520 MPa at 500 °C, 319 MPa at 600 °C and 56 MPa at 700 °C. Results indicated that the creep rates in nitrogen and of the coated alloy were lower than those of the uncoated in air.