Fracture behavior and mechanical properties of Mg–4Y–2Nd–1Gd–0.4Zr (wt.%) alloy at room temperature

The microstructure, mechanical properties and fracture behavior of gravity die cast Mg–4Y–2Nd–1Gd–0.4Zr (wt.%) (WNG421) alloy are studied at room temperature in different thermal conditions, including as-cast, solution-treated and different aging-treated (both isothermal and two-step aging) conditions. The results indicate that WNG421 alloy shows different behaviors of crack initiation and propagation in different thermal conditions during tensile test at room temperature. After pre-aged at 200 °C for 5 h, the hardness of WNG421 alloy first reduces and then increases when secondary aged at 250 °C (two-step aging). The peak hardness and corresponding tensile strength of the two-step aged alloy both increases compared with those in 250 °C isothermal peak-aged condition. Tensile strength of WNG421 alloy at room temperature in low temperature (200 °C) isothermal peak-aged condition is much higher than that in high temperature (250 °C) isothermal peak-aged condition.