Compressive creep behavior of as-cast and aging-treated Mg–5 wt% Sn alloys

The microstructure and compressive creep behaviors of as-cast and aging-treated Mg–5 wt% Sn alloys are investigated in this paper. The compressive creep resistance of aging-treated Mg–5 wt% Sn alloy is much better than that of as-cast alloy at the applied stresses from 25 MPa to 35 MPa and the temperatures from 423 K to 473 K, which is mainly due to the dispersive distribution of Mg2Sn phase in the aging-treated Mg–5 wt% Sn alloy. The calculated average values of stress exponent n and activation energy Qc suggest that dislocation cross slip and dislocation climb happen respectively in as-cast and aging-treated Mg–5 wt% Sn alloys during creep.