A Mg–Al–Nd alloy produced via a powder metallurgical route

A Mg–5 wt.%Al–2 wt.%Nd alloy has been prepared by a powder metallurgical route using a blend of two dissimilar alloy powders. The initial consolidation of the powders was achieved through a single equal channel angular extrusion pass at 150 °C. After heat treatment at temperatures between 420 °C and 530 °C, it was possible to produce a microstructure that consisted of a uniform distribution of Al3Nd and Al11Nd3 precipitates in a magnesium matrix. These precipitates displayed distinct orientation relationships with the matrix. The size and shape of the precipitates depended on the heat treatment temperature and time.