Effect of Mg17Al12 precipitates on the microstructural changes and mechanical properties of hot compressed AZ91 magnesium alloy

During hot compression, Mg17Al12 (β) precipitates show strong influence on the microstructural changes of 415 °C-24 h homogenized AZ91 alloy. When compressed at 300 °C and 350 °C, dynamic recrystallization (DRX) only occurs near grain boundaries with discontinuous β precipitate pinning at the newly DRXed grain boundaries. With increasing compression temperature and decreasing strain rate, the β-precipitating region expands; however, the amount of pinning precipitates decreases, resulting in increases in the DRX ratio and average DRXed grain size. With a compression ratio of only 50%, the specimen compressed at 350 °C and a strain rate of 0.2 s−1 (designated 350 °C-0.2 s−1 compressed specimen) shows an ultimate tensile strength (UTS) of 334 MPa, a 0.2% proof stress (PS) of 195 MPa and an enough elongation of 17.9%. After a subsequent aging treatment at 180 °C, due to the large number of β precipitates, the strength of the compressed specimens are further improved, and the specimen peak aged after compression at 400 °C and 0.2 s−1 shows UTS of 364 MPa and PS of 248 MPa with a moderate elongation of 7.7%.