Scaling exponents for fracture surfaces in opal glass

We have investigated the scaling properties of fracture surfaces in opal glass. Specimens with two different opacifying particle sizes (1 μm and 0.4 μm) were broken by three-point bending test and the resulting fracture surfaces were analyzed using Atomic Force Microscopy. The analysis of the self-affine behavior was performed using the Variable Bandwidth and Height–Height Correlation Methods, and both the roughness exponent, ζ, and the correlation length, ξ, were determined. It was found that the roughness exponent obtained in both samples is ζ ∼ 0.8; whereas the correlation length in both fractures is of the order of the particle size, demonstrating the dependence of this self-affine parameter on the microstructure of opal glass.