Synchrotron micro-diffraction analysis of the microstructure of cryogenically treated high performance tool steels prior to and after tempering

The phase transformation and strain changes within cryogenically (−196 °C) treated high performance tool steels (AISI H13) before and after tempering have been examined using both laboratory XRD and synchrotron micro-diffraction. The martensitic unit cell was found to have very low tetragonality as expected for low carbon steel. Tempering resulted in the diffusion of excess carbon out of the martensite phase and consequent unit cell shrinkage. In addition on tempering the martensite became more homogeneous as compared to the same samples prior to tempering. For cryogenically treated samples, the effect was most pronounced for the rapidly cooled sample which was the least homogenous sample prior to tempering but was the most homogenous sample after tempering. This suggests that the considerable degree of disorder resulting from rapid cryogenic cooling results in the beneficial release of micro-stresses on tempering thus possibly resulting in the improved wear resistance and durability observed for cryogenically treated tool steels.