The effects of post annealing on the mechanical properties, microstructure and texture evolutions of pure copper deformed by twist extrusion process

X-ray diffraction peak broadening analysis showed that performing a proper heat treatment between the twist extrusion passes of commercially pure copper decreased the coherent domain size and increased the microstrain. Moreover, SEM micrographs illustrated that annealed material contained new formed grains that could not grow due to lack of sufficient time. Under such circumstances, the ultimate strength was elevated about 45 MPa. The deformed material showed texture of simple shear deformation, changing by applying the post annealing.