Failure assessment of notched polycrystalline graphite under tensile-shear loading

The fracture load and the fracture initiation angle were experimentally measured for a V-notched specimen made of polycrystalline graphite under combined tensile-shear loading. The experimental results were obtained for several specimens with different notch angles and various notch tip radii. The experimental observations showed that for a constant notch tip radius, the fracture load in pure tensile loading conditions decreases as the notch angle increases. Moreover, for a constant notch angle, as the notch tip radius increases the fracture load in graphite specimens enhances in the entire domain between pure tensile and pure shear loading conditions. A recently developed failure criterion was then used to estimate the experimental values of the notch fracture resistance and the fracture initiation angle for the tested graphite specimens. The experimental results could be estimated very well by using the results of the proposed criterion.