Deformation band and texture of a cast Mg–RE alloy under uniaxial hot compression

Microstructural evolution and texture of a cast Mg–9Gd–4Y–0.6Zr ingot under hot compression were studied in this paper. Post-deforming microstructures were characterized by optical microscopy, scanning electron microscopy and transmission electron microscopy, while crystallographic orientation information was obtained from X-Ray macro-texture measurement and EBSD micro-texture analysis. Dynamic recrystallization (DRX) initiated from the deformation bands (DB) forming on original grain boundaries; the DB became widen with continuously conversion of low-angle-boundary grains into high-angle-boundary grains. The tendency of strain localization increased with Z parameter. The macro-texture analysis indicates that uniaxial compression yielded out the randomized basal texture component. This texture component was found to be strengthened with increasing Z parameter. The micro-texture analysis shows that the deviation from the ideal basal texture arose from orientated growth within DBs. Moreover, the localization deformation promoted dynamic precipitation within DBs, which inhibited the development of DRX.