Properties of geopolymer with seeded fly ash and rice husk bark ash

In the present work, compressive strength of inorganic polymers (geopolymers) produced of seeded fly ash and rice husk bark ash has been investigated. Different specimens made from a mixture of fly ash and rice husk bark ash in fine and coarse form were subjected to compressive strength tests at 7 and 28 days of curing. The curing regime was different: one set of the specimens were cured at room temperature until reaching to 7 and 28 days and the other sets were oven cured for 36 h at the range of 40–90 °C and then cured at room temperature until 7 and 28 days. The results indicate that in both 7 and 28 days regimes, the highest strengths are related to the specimens by SiO2/Al2O3 ratio equals 2.99 cured at 80 °C. For these specimens, those contained finer fly ash particles show more compressive strength. Thermogravimetric analysis and Fourier transform infrared spectroscopy both also are in agreement with the obtained results from compressive strength tests. In addition, SEM micrographs of the specimens show that the finer the particle size of the utilized ashes, the denser the microstructure which confirms the results obtained by the strength tests.