Effect of hot compressive deformation on the martensite transformation of Ti–10V–2Fe–3Al titanium alloy

The hot deformation behavior of as-cast TB6 alloy was investigated by isothermal hot compressive deformation from 800 °C to 1150 °C at the strain rates between 10−3 s−1 and 10 s−1. The microstructural evolution of martensite transformation of the deformed TB6 was observed, and the volume fraction of martensite was also studied. The results show that the deformation temperature plays an important role on the stress-induced martensite transformation for TB6 titanium alloy. When the strain rate is 0.001 s−1, 0.01 s−1, 0.1 s−1, 1 s−1, and 10 s−1, the deformation temperature with more martensite content is 900–975 °C, 925–1050 °C, 825–1100 °C, 910–1000 °C, and 925–1100 °C, respectively.