On the use of accumulative roll bonding process to develop nanostructured aluminum alloy 5083

In the present study, the effect of accumulative roll bonding (ARB) process at room temperature on the microstructure and mechanical properties of AA5083 strip was investigated. Microstructural observations were done by transmission electron microscopy (TEM) and scanning electron microscopy (SEM). Also, mechanical properties were performed by tensile, hardness, and microhardness tests. It was observed that accumulative roll bonding is a promising process for production of nanostructured (80 nm) AA5083 strips. Nano shear bands were formed in the microstructure after the fourth cycles. When the number of cycles increased, the tensile strength and hardness of the accumulatively roll bonded strips increased. However, by increasing the number of cycles, the elongation value decreased except for the last (sixth) cycle. It was found that when the number of cycles increased, the distribution of microhardness values became more uniform. After the tensile test, debonding can be observed especially in the interface formed in the last cycle. Observations revealed that the failure mode in the accumulatively roll bonded AA5083 strip was a shear ductile rupture with elongated shallow shear dimples.