High strength aluminum cast alloy: A Sc modification of a standard Al–Si–Mg cast alloy

A standard Aluminum–Silicon–Magnesium cast alloy (A357 foundry alloy without Beryllium) modified with different weight percentages of Scandium (Sc), has been studied to evaluate the effects of Sc contents on microstructure and strength. Study has been conducted under optimized parameters of melting, casting and heat treatment. Characterization techniques like optical microscopy, SEM, TEM and tensile testing were employed to analyze the microstructure and mechanical properties. Results obtained in this research indicate that with the increase of Sc contents up to 0.4 wt%, grain size is decreased by 80% while ultimate tensile strength and hardness are increased by 28% and 19% respectively. Moreover along with the increase in strength, elongation to failure is also increased up to 165%. This is quite interesting behavior because usually strength and ductility have inverse relationship.