Electrical Discharge Surface Alloying of Ti and Fe Workpiece Materials Using Refractory Powder Compact Electrodes and Cu Wire

The paper reviews the use of metal powders dispersed in the dielectric fluid and refractory PM electrodes, to initiate workpiece surface modification during EDM. Experimental work details the effects of EDM parameters (up to 270 V) on the hardness/composition of the white layer following die sink machining of AISI H13 tool steel and roll texturing of 2% Cr steel using partially sintered PM electrodes. Similar data are presented following EDM scanning and wire cutting of standard TI alloy TI-6AI-4V and a y TIAI. With AISI H13, recast layers were 5-20 μm thick and up to ∼ 1350 HK0.025. When machining TI-6AI-4V with WC/Co electrodes, recast microhardness was 600-2900 HK0.025. Wire cutting y TIAI generated porous alloyed layers up to 115 μm thick with extensive cracks and no increase in bulk hardness.