Analysis of the microstructure near the crack tip of ASME Gr.92 steel after creep crack growth

The microstructures near to and remote from the tip of a crack in ASME Gr.92 steel were investigated after creep crack growth at 873 and 898 K, focusing on the martensitic lath, the dislocation structure, and precipitates. After creep, the mean lath width near the crack tip was obviously larger than that of the virgin material, whereas the lath width remote from the crack tip was only slightly larger than that of the virgin material. The mean dislocation density near the crack tip markedly decreased after creep, whereas only a small change was observed in the dislocation density remote from the crack tip. The mean size of M23C6 particles near the crack tip after creep was larger than that of the virgin material, whereas their mean size remote from the crack tip was almost the same as that of the virgin material.