Effect of cooling rate and Mg content on the Al–Si eutectic for Al–Si–Cu–Mg alloys

This study investigates and clarifies the qualitative and quantitative effects of Mg content and cooling rate (ranging from 0.5 to 4 °C/s), on the modification of the silicon eutectic structure and on the undercooling of the silicon eutectic growth temperature (ΔTSi-eut) in the series of Al–Si–Cu–Mg alloys. The critical Mg content to produce a notable improvement in the silicon eutectic by 1.5 modification levels (regardless of the cooling rate) is 0.6 wt.% Mg. A similar increase in the modification level was also observed when the cooling rate was increased to a maximum of 4 °C/s, regardless of the Mg content. Measurements of the area and roundness of the silicon particles showed a good correlation with the modification level. The undercooling (ΔTSi-eut) increased by up to ~ 23 °C at a relatively high Mg content and cooling rate and up to ~ 14 °C when the Mg content was increased from 0.4 to 0.6 wt.%.