The effect of porcelain thickness and surface liner application on the fracture behavior of a ceramic system

Objectives ermine the effect of porcelain thickness and the application of a surface liner (SL) on the flexural strength (σ) of a ceramic system. s ndred twenty bar-shaped specimens of yttria-stabilized zirconia-based ceramic were fabricated and randomly divided into two groups according to the application of SL: A – applied; B – not applied. The specimens were further divided according to the porcelain veneer thickness (n = 20): 0–0.5 mm; 1–1.0 mm; 2–2.0 mm. All specimens were tested in 3-point bending with the porcelain under tension. The maximum load was recorded at first sign of fracture, the σ was calculated and the mode of failure was determined. Data was statistically analyzed using one-way ANOVA, Tukey (α = 0.05) and Weibull distribution. s application had no effect (p = 0.723) while the porcelain thickness had a significant effect (p = 0.000) on the mean σ values. No significant differences in mean σ values were found with same porcelain thickness. A 0.5-mm thick porcelain layer (groups A0 and B0) showed greater mean σ values than other groups. The Weibull modulus (m) ranged from 6 (groups A1 and B2) to 9 (groups A0, A2 and B0). The predominant mode of failure for all groups was fracture initiation at the porcelain surface propagating to the ceramic interface. icance rcelain thickness influenced the mean σ values, but the SL had no significant effect on the flexural strength and the mode of failure of the ceramic system examined.