Caries-preventive effect of sealants produced with altered glass-ionomer materials, after 2 years

Objectives m of the present study was to investigate the caries-preventive effect of sealants produced with a high-viscosity glass-ionomer with an elevated powder-liquid ratio (ART), of having energy added to this glass-ionomer, and that of glass-carbomer, in comparison to that of resin composite sealants. s ndomized controlled trial covered 407 children, with a mean age of 8 years. At a school compound three dentists placed sealants in pits and fissures of high caries-risk children. Evaluation by two independent evaluators was conducted after 0.5, 1 and 2 years. The Kaplan–Meier survival method, ANOVA and t-test were used in analyzing the data. s irst permanent molars were sealed. 6.6% of children and 6.8% of sealants dropped out within 2 years. 27 re-exposed pits and fissures, 20 in occlusal and 7 in smooth surfaces, in 25 children, developed a dentin carious lesion. The cumulative survival of dentin carious lesion-free pits and fissures in the glass-carbomer sealant group was statistically significantly lower (97.4%) than those in the high-viscosity glass-ionomer with energy supplied (99%) and the resin-composite (98.9%) sealant groups. There was no statistically significant difference in the cumulative survival of dentin carious lesion-free pits and fissures, between the high-viscosity glass-ionomer with (99%) and without (98.3%) energy supplied sealant groups, after 2 years. icance rvival of dentin carious lesion-free pits and fissures was high in all sealant types. More dentin carious lesions were observed in the glass-carbomer sealant group.