Failure analysis of a hydro-processing reactor
Author/Authors
Wang، نويسنده , , Yang and Lu، نويسنده , , Ye-Bo and Pan، نويسنده , , Hong-Liang، نويسنده ,
Issue Information
روزنامه با شماره پیاپی سال 2009
Pages
8
From page
11
To page
18
Abstract
Analyzed is the failure of a stainless steel (SS) hydro-processing reactor that is used for flavor-fragrance test. It is found that the cracks on the reactor wall are typical of stress corrosion cracking caused by chloride from the process catalyst. Recommendations are made to mitigate the aforementioned cracking failure.
Keywords
Catalyst , chloride , Hydro-processing reactor , Failure analysis , Stress corrosion cracking (SCC)