Determination of the length dependence of the threshold for fatigue crack propagation

A rising load amplitude crack growth test on specimens pre-cracked in cyclic compression is presented as a procedure to determine the length dependence of the threshold of fatigue crack propagation described by the R(resistance)-curve for the threshold of stress intensity factor range. The experimental results show that the residual stress field in front of the pre-crack can significantly influence the R-curve. er to measure the material specific R-curve which is not affected by the pre-cracking condition it is important to use the smallest possible load amplitude. To achieve this goal, a very small notch root radius is essential. It is shown that at notches machined by razor blade polishing technique the load amplitude for pre-cracking can be reduced to values where the load history does not influence the R-curve for the threshold of stress intensity range.