Analysis of the unstable fracture behaviour of a high strength low alloy steel weldment

Local brittle zones (LBZ) cause the unstable fracture behaviour of weld metals. This threatens the safe service of welded structures and makes structural assessment procedures difficult. Therefore, the unstable fracture behaviour of an overmatched high strength low alloyed steel weldment was experimentally investigated. It showed that any interaction between two adjacent weld metal matrix and soft weld metal inclusions produces LBZ, causing local unstable fracture behaviour. The formation of a low hardness region is attributed to the multipass welding reheating process between Ac1 and the self-tempering temperature. The presence of partly solid metallic inclusions with a high content of alloying elements and pro-eutectoid ferrite microstructure were found to be additional causes for the local unstable fracture behaviour of the weld metal. Local strength mis-match induced the yielding and strain hardening in the soft weld metal inclusions, contributing significantly to unstable fracture behaviour. Thus, a significantly different scatter of experimental results can be obtained. In the cases of specimens with through-the-thickness crack, not only is the scatter significantly lower, but the toughness itself.