An experimental investigation on fatigue crack growth of AL6XN stainless steel

The crack growth behavior of AL6XN stainless steel was experimentally investigated using round compact tension (CT) specimens. The influences of the R-ratio (the ratio of the minimum load over the maximum applied load in a cycle), the tensile and compressive overloads, and the loading sequence on crack growth were studied in detail. The results from the constant-amplitude experiments show a sensitivity of the crack growth rate to the R-ratio. The application of a tensile overload has a profound effect on crack growth, resulting in a significant retardation in the crack propagation rate. A compressive overload (underload) leads to a short-lived acceleration in crack growth. Results from the two-step high–low loading reveal a period of crack growth retardation at the beginning of the lower amplitude step, an effect similar to that of a single overload. A crack driving force parameter together with a modified Wheeler model is found to correlate the crack growth experiments well.