Electrical failure of piezoelectric ceramics with a conductive crack under electric fields

The failure behavior of piezoelectric ceramics with a conductive crack under purely electric loading is investigated. Electrical fracture tests are conducted to study the influence of the directions of poling and electric loading. Two failure modes of piezoelectric materials are observed: fracture that is accompanied with dielectric discharging and the formation of tubular channels without fracture. The critical J integrals at the onset of both fracture and breakdown are calculated numerically via finite element analysis. The effects of both the direction of the electric field and the poling direction on both fracture and breakdown resistance are discussed.