Analytical study of fatigue crack growth in AA7050 notched specimens under spectrum loading

An analytical study of fatigue crack growth in aluminium alloy 7050-T7451 notched specimens under a fighter aircraft wing root bending moment spectrum was conducted. The crack growth data were measured by quantitative fractography for three groups of specimens with different stress concentration geometrical features. Under spectrum loading and for each spectrum peak stress level, a minimum of five specimens were tested. Based on the analysis of the measured spectrum crack growth data using linear elastic fracture mechanics, it was found that the concept of geometry factors formulated in the stress intensity factor could not collapse the crack growth rate data derived from each stress concentration feature, particularly near the small crack growth region. In order to investigate the possible reasons for this, three-dimensional elastic–plastic finite element analysis was used to determine notch plastic zone sizes for each stress concentration geometry. As a consequence, an alternative crack growth driving force by considering both notch elastic–plastic stress field and gross net-section stress field was proposed and used to interpret the fatigue crack growth data under spectrum loading. It was found that the predictions of crack growth under spectrum loading for different stress concentration factors at different peak load levels agree reasonably well with the experimental results.