Constraint loss correction for assessment of CTOD fracture toughness under welding residual stress. Part I: Methodology using the equivalent CTOD ratio

This part I of a two-part paper presents a method of assessing the effects of welding residual stress and constraint loss on the cleavage fracture of a wide plate subjected to membrane stress based on the Weibull stress criterion. It has been found that the Weibull stress criterion is efficient for evaluating the fracture instability of wide plates with and without a welding residual stress field. The concept of an equivalent crack-tip opening displacement (CTOD) ratio β r under a welding residual stress field is introduced for assessment of constraint loss effects on CTOD fracture toughness of wide plates. The equivalent CTOD ratio β r is defined as the ratio of the CTOD in the standard fracture toughness specimen to the CTOD in a wide plate with a welding residual stress at the same level of the Weibull stress. Fracture assessment procedures using β r for wide plates are shown within the framework of the failure assessment diagram. It has been found that the excessive conservatism observed in the conventional procedure can be reduced reasonably by applying the proposed method. The companion part II of the paper presents applications of the CTOD toughness correction method using β r to the fracture test data of welded joints and verifies the proposed method in the ductile–brittle transition temperature region.