Simulation of residual thermostress in tungsten after repetitive ELM-like heat loads

Brittle destruction of tungsten armour under action of edge localised modes of plasma instabilities (ELMs) in ITER is an important issue determining the lifetime of the divertor. Besides, cracking of the armour produces tungsten dust with characteristic size of 1–10 μm flying from the armour surface with velocities up to 10 m/s. Influx of the tungsten dust into the ITER confinement decreases the temperature of the plasma, reduces the thermonuclear gain and even may run the confinement into disruption. aper describes experiments in QSPA-Kh50 plasma gun and modeling, which has been performed for providing more insight into the physics of tungsten cracking under action of ELMs and for confirmation of the important result on stabilization of the crack development at the tungsten armour surface, predicted in our previous paper – the same authors, 2010. reshold value of energy density deposition for start of tungsten cracking has been measured as 0.3 MJ/m2 after 5–10 shots. From analytical considerations three times smaller threshold value has been predicted with increasing number of shots.