Cracking susceptibility of stainless steel subjected to plasma disruption

The similarities and differences in the cracking susceptibility between welding and resolidification after plasma disruption were examined experimentally using a number of primary candidate alloy samples with different chemical compositions. The product of the number density and the average depth of the cracks was measured after simulated disruption, employing a hydrogen ion beam as the heat source, and was compared with the Varestraint test result. An adequate correlation was observed between them, which indicates that the cracking susceptibility during plasma disruption can be well estimated from the welding cracking susceptibility.