Title of article :
Ethanol-based Tape Casting Process of the Textured Bi0.5(Na0.80K0.20)0.5TiO3-BiFeO3 Ceramics
Author/Authors :
Moosavi, A Department of Semiconductors - Materials and Energy Research Center, Karaj , Bahrevar, M. A Department of Semiconductors - Materials and Energy Research Center, Karaj , Aghaei, A. R Department of Semiconductors - Materials and Energy Research Center, Karaj
Abstract :
The rheological and tape casting behavior of ethanol-based Bi0.5(Na0.80K0.20)0.5TiO3-7 mol% BiFeO3
(BNKT-BF) slurries was investigated. The effect of sintering temperature profile on texture
development with a preferred <001> orientation was also studied. A 50 MPa pressure assisted three
step sintering profile promoted extensive texture development together with densification. The role of
BF as a sintering promoter has been discussed.
Farsi abstract :
در اين پژوهش رفتار رئولوژيكي دوغاب‌هاي حاوي ذرات پيزوالكتريك بدون سرب بر پايه تيتانات بيسموت سديم پتاسيم به همراه 7 درصد مولي نانو ذرات فريت بيسموت با فرمول شيمياييBi0.5(Na0.80K0.20)0.5TiO3-7 mol% BiFeO3 (BNKT-BF) مورد بررسي قرار گرفت. نانو ذرات فريت بيسموت به همراه ذرات BNKT به كمك روش ريخته‌گري نواري به همراه ذرات صفحه‌اي شكل تيتانات بيسموتBi4Ti3O12 (BIT) به عنوان شابلون، براي رسيدن به ريزساختار بافت‌دار استفاده شدند. ريزساختار بافت‌دار با رشد ترجيحي ذرات، توسط برنامه‌هاي تف جوشي متقاوتي بررسي و سرانجام با اعمال فشار 50 مگاپاسكال در دماي ◦C 800 و حرارت دهي مجدد در دمايC ◦ 1200 به مدت 10 ساعت ريزساختار بافت‌دار حاصل شد.
Keywords :
Texture , BNKT , Sintering , BiFeO3 , Slurry
Journal title :
Astroparticle Physics