In vitro evaluation of coronal discoloration following the application of calcium‑enriched mixture cement, Biodentine, and mineral trioxide aggregate in endodontically treated teeth

Background: This study sought to assess and compare coronal discoloration following the application of white mineral trioxide aggregate, Biodentine, and calcium‑enriched mixture cement in endodontically treated teeth. Materials and Methods: In this in vitro experimental study, 64 freshly extracted sound human premolars were selected, cleaned, and stored in saline. After cleaning, shaping, and obturation the root canal of the teeth, the teeth were randomly assigned to one control (n = 4) and three experimental (n = 20) groups. In the experimental groups, the cement were applied over the canal orifices in 3‑mm thickness. All teeth were then restored with composite resin. Color parameters, according to the CIE L*a*b* system, were measured using Vita Easyshade spectrophotometer before application of cement and at 1 week, 1 month, 2 months, and 3 months after the application of cement. The recorded values were statistically analyzed using descriptive and analytical statistics. For analytical statistics, Kolmogorov–Smirnov test was applied to assess normal distribution of data. ANOVA was used to compare the results at baseline and repeated measures. P < 0.05 was considered statistically significant Results: Significant differences were noted in color change (ΔE) between all time points except between ΔE4 (2 months) and ΔE5 (3 months) (P < 0.01). However, tooth discoloration caused by the three cement was not significantly different (P = 0.343). Conclusion: The three tested cement were not significantly different in terms of causing coronal discoloration in endodontically treated teeth.