Highly efficient nitrobenzene photoreduction over the amino acid-modified CdS-TiO2 nanostructures under visible light

Cd-Scoupled TiO2 nanocrystals were prepared by the microemulsionmediated solvothermal method at pretty low temperatures. The semiconductor nanocrystals were modified with tyrosine, phenyl alanine, glysine and glutamate aminoacids and then were characterized by BET, SEM, EDX, XRD, UV–Vis spectroscopy, and FTIR analysis methods. The specific surface area and the average pore diameter were found to be about 470 m² g^−1 and 2.8 nm, respectively. Moreover, the average size of the CdSTiO2 particles was evaluated to be 28 nm. The results showed that the modification process with the aminoacids improves the adsorption capability and photoactivity of the samples. Among them, tyrosine was determined to be the best choice. According to the results, modification of CdSTiO2 heterojunction photocatalyst with electrondonating groups is an efficient strategy to increase the photoreduction of nitroaromatic compounds. Reusability experiments were also carried out and confirmed the high capacity of the prepared samples for the photoconversion of nitrobenzene after being repeated for four times.