Author/Authors :
WAN JALAL, WAN NASARUDIN Universiti Kebangsaan Malaysia - Faculty of Engineering and Built Environment - Department of Electrical, Electronic and System Engineering, Malaysia , ABDULLAH, HUDA Universiti Kebangsaan Malaysia - Faculty of Engineering and Built Environment - Department of Electrical, Electronic and System Engineering, Malaysia , ZULFAKAR, MOHD SYAFIQ Universiti Kebangsaan Malaysia - Faculty of Engineering and Built Environment - Department of Electrical, Electronic and System Engineering, Malaysia , SHAARI, SAHBUDIN Universiti Kebangsaan Malaysia - Institute of Microengineering and Nanoelectronics (IMEN), Malaysia , ISLAM, MOHAMMAD THARIQUL Universiti Kebangsaan Malaysia - Institute of Space Science (ANGKASA), Malaysia , BAIS, BADARIAH Universiti Kebangsaan Malaysia - Faculty of Engineering and Built Environment - Department of Electrical, Electronic and System Engineering, Malaysia
Abstract :
CaxZn (1-x)Al2O4 thin films (x = 0.00; 0.05; 0.10; 0.15 and 0.20) were prepared by sol-gel method with the substitution of Zn^2+ by Ca^2+ in the framework of ZnAl2O4. The effect of Ca addition on the structure and morphology of CaZnAl2O4 thin films was investigated by x-ray diffraction (XRD), field-emission scanning electron microscope (FESEM), energy-dispersive x-ray spectroscopy (EDX), ultra-violet visible (UV-Vis) and atomic force microscope (AFM). The XRD patterns showed the characteristic peaks of face-centred cubic (fcc) ZnAl2O4 and CaZnAl2O4. The addition of Ca increased the crystallite size from 8.9 to 30.2 nm. The bandgap of CaxZn(1-x)Al2O4 thin film was found in the range of 3.40 to 3.84 eV. SEM micrograph shows the morphology of all thin films is sphere-like, with the grain size increased from 33 to 123 nm. The AFM images show the roughness of surface morphology increased. The substitution of Zn^2+ by Ca^2+ increased the crystallite size, grain size and surface roughness which evidently increased the density (4.59 to 4.64 g/cm^3) and dielectric constant (8.48 to 9.54). The composition of CaxZn(1-x)Al2O4 is considered as suitable material for GPS patch antennas.
Keywords :
Band gap , Ca , ZnAl2O4 , GPS patch antena , nanostructures