Title of article
Characteristics of hydrogen embrittlement, stress corrosion cracking and tempered martensite embrittlement in high-strength steels
Author/Authors
N. Eliaz، نويسنده , , A. Shachar، نويسنده , , B. Tal and D. Eliezer، نويسنده ,
Issue Information
روزنامه با شماره پیاپی سال 2002
Pages
18
From page
167
To page
184
Keywords
Structural steel , stress-corrosion cracking , Hydrogen embrittlement , Tempered martensite embrittlement , Failure analysis
Journal title
Engineering Failure Analysis