Evaluation of the stability and durability of Pt and Pt–Co/C catalysts for polymer electrolyte membrane fuel cells

Carbon supported Pt and Pt–Co nanoparticles were prepared by reduction of the metal precursors with NaBH4. The activity for the oxygen reduction reaction (ORR) of the as-prepared Co-containing catalyst was higher than that of pure Pt. 30 h of constant potential operation at 0.8 V, repetitive potential cycling in the range 0.5–1.0 V and thermal treatments were carried out to evaluate their electrochemical stability. Loss of non-alloyed and, to a less extent, alloyed cobalt was observed after the durability tests with the Pt–Co/C catalyst. The loss in ORR activity following durability tests was higher in Pt–Co/C than in Pt/C, i.e. pure Pt showed higher electrochemical stability than the binary catalyst. The lower stability of the Pt–Co catalyst during repetitive potential cycling was not ascribed to Co loss, but to the dissolution–re-deposition of Pt, forming a surface layer of non-alloyed pure Pt. The lower activity of the Pt–Co catalyst than Pt following the thermal treatment, instead, was due to the presence of non-alloyed Co and its oxides on the catalyst surface, hindering the molecular oxygen to reach the Pt sites.